Thermoplastic Urethane (TPU) Material Product Data Sheet

Select the material type below:

Typical Properties Data Sheet
Polyurethane - Extrusion - Polyether

		ENGLISH
GENERAL	ASTM TEST	VALUES	UNITS
Specific Gravity/Density	D-792	1.14	lb/ft³
Mold Shrinkage 1/8" Bar	D-956	.011 - .015	in/in
Hardness, Rockwell	D-785	85A	--
Reinforcement Content			%
Water Absorption (24 hr.)	D-570	1.2	%
MECHANICAL
Ultimate Tensile Strength	D-412	4,200	psi
Ultimate Elongation @ Break	D-412	600	%
Flexural Modulus	D-790	10,000	psi x 10⁵
Flexural Strength	D-790		psi
Tear Strength	D-624	470 (82,297)	Pli (n/m)
Elongation Set After Break	D-412	80	%
Compression Set 22Hrs @ 77 degrees F	D-395	25	%
Taber Abrasion H-22 Wheel	D-1044	5	mg
Tensile Modulus @ 50% Elongation	D-412	800	psi (Mpa)
Tensile Modulus @ 100% Elongation	D-412	900	psi (Mpa)
Tensile Modulus @ 300% Elongation	D-412	1550	psi (Mpa)
	UL94
	UL94
RHEOLOGICAL PROPERTIES
Melt Flow Rate MFR 190 C/8.7 kg	D-1238	20	g/10 min

Typical Properties Data Sheet
Polyurethane - Molding Grade - Polyester

		ENGLISH
GENERAL	ASTM TEST	VALUES	UNITS
Specific Gravity/Density	D-792	1.18	lb/ft³
Mold Shrinkage 1/8" Bar	D-956	.011 - .015	in/in
Hardness, Rockwell	D-785	85A	--
Reinforcement Content			%
Water Absorption (24 hr.)	D-570	1.2	%
MECHANICAL
Ultimate Tensile Strength	D-412	5,000	psi
Ultimate Elongation @ Break	D-412	500	%
Flexural Modulus	D-790	10,000	psi x 10⁵
Flexural Strength	D-790		psi
Tear Strength	D-624	500	Pli (n/m)
Elongation Set After Break	D-412	50	%
Compression Set 22Hrs @ 77 degrees F	D-395	25	%
Taber Abrasion H-22 Wheel	D-1044	50	mg
Tensile Modulus @ 50% Elongation	D-412	850	psi (Mpa)
Tensile Modulus @ 100% Elongation	D-412	1050	psi (Mpa)
Tensile Modulus @ 300% Elongation	D-412	2100	psi (Mpa)
	UL94
	UL94
RHEOLOGICAL PROPERTIES
Melt Flow Rate MFR 224 C/.2 kg	D-1238	30	g/10 min